PTFE GRAPHITE PACKINGS
| ITK® STYLE 212 PTFE Graphite Fibre packing (With High Graphite Content) Product Description ITK® style 212 is square braided constructed from best quality PTFE Graphite fibre packing, This packing is manufactured from PTFE fibres fixed closely together with graphite fibres through a unique process of incorporation and further treated with special lubricant capable of withstanding higher temperatures. |
 |
Service Characteristics
|
Service Characteristics
|
|
|
Temperature: -200°C to +280°C
|
pH Range: 0 to 14
|
|
Rotary Shaft Speed: 23m/s
|
Pressure: 120bar or 1740psi
|
Typical Application Areas
This universal packing can be used in nearly all static, rotary and reciprocating uses.
| ITK® STYLE 212A PTFE packing blended with Graphite yarns and treated with lubricants Product Description ITK® style 212A is square braided constructed from PTFE Yarn, This packing is manufactured from PTFE fibres fixed closely together with graphite fibres through a unique process of incorporation and further treated with special lubricant capable of withstanding higher temperatures. |
 |
Service Characteristics
|
Service Characteristics
|
|
|
Temperature: -200°C to +280°C
|
pH Range: 0 to 14
|
|
Rotary Shaft Speed: 23m/s
|
Pressure: 120bar or 1740psi
|
Typical Application Areas
This universal packing can be used in nearly all static, rotary and reciprocating uses.
| ITK® STYLE 208 100 % Unsintered PTFE Valve Stem packing Product Description ITK® style 208 is manufactured from 100% unsintered Pure Virgin PTFE Resin, This packing is a pliable and self-lubricating packing that eliminates stem wear and last longer. ITK® style 208 has very high tensile strength and flexible gasket material impervious to gases and liquids after compression. |
 |
Service Characteristics
|
Service Characteristics
|
|
|
Temperature: -100°C to +250°C
|
pH Range: 0 to 14
|
|
Rotary Shaft Speed: 1m/s
|
Pressure: 120bar or 1740psi
|
Typical Application Areas
Its ideal for use in process lines in chemical processing plants and petroleum refineries.